Influence of Filler Materials on Pinned Joints of Woven Glass Fiber Reinforced Epoxy Composites 

Authors

  • H.M. Harsha Department of Mechanical Engineering, GM Institute of Technology, Davangere, Karnataka, India
  • M.C. Murugesh Department of Mechanical Engineering, GM Institute of Technology, Davangere, Karnataka, India
  • K.N. Bharath Department of Mechanical Engineering, GM Institute of Technology, Davangere, Karnataka, India

DOI:

https://doi.org/10.12974/2311-8717.2013.01.01.6

Keywords:

Polymer Matrix Composites, Pinned joints, Fillers, Failure load.

Abstract

Fiber reinforced composite materials have been gaining wide application in aircraft submarine and spacecraft constructions, to strengthen bridges and other civil engineering structures. Joints are formed using mechanical fasteners and load sharing in these joints depends on the number, size, and material of the bolts and the stiffness of the joining members. Therefore, suitable revealing methods for the failure strength would help in selecting the appropriate joint size in a given application.

The objective of the present work is to determine the bearing or failure load of filler added woven glass fiber/epoxy composites through single and double serial pinned joints with different parameters by experimental methods. The effect of the distance from free edge to the diameter of first hole (E/D) ratio, the width of plate to diameter of hole (W/D) ratio and the effect of filler materials on Titanium dioxide (TiO2) and Zinc Sulphide (ZnS) on bearing load are experimentally investigated using laminated woven glass fiber composite plate with single and double serial pinned joints. 

References

Aktas A. Failure analysis of serial pinned joints in composite materials. IJEMS 2011; 18: 102-10.

Aktas A, Imrek H, Cunedioglu Y. Experimental and numerical failure analysis of pinned-joints in composite materials. J Compos Mater 2009; 89: 459-66.

Karakuzu R, Caliskan CR, Aktas M, Icten BM. Failure behavior of laminated composite plates with two serial pinloaded holes. Compos Struct 2008; 82: 225-34. http://dx.doi.org/10.1016/j.compstruct.2007.01.002

Dano M-L, Gendron G, Picard A. Stress and failure analysis of mechanically fastened joints in composite laminates. Compos Struct 2000; 50: 287-96. http://dx.doi.org/10.1016/S0263-8223(00)00119-7

Lin HJ, Tsai CC, Shie JS. Failure analysis of woven-fabric composites with moulded-in holes. Compos Sci Tech 1995; 55: 231-39. http://dx.doi.org/10.1016/0266-3538(95)00091-7

Nanda Kishore A, Malhotra SK, Siva Prasad N. Failure analysis of multi-pin joints in glass fiber/epoxy composite laminates. J Compos Mater 2009; 91: 266-77.

Icten BM, Okutan B, Karakuzn R. Failure strength of Woven glass fiber-epoxy composite pinned joints. J Compos Master 2003; 37(15): 1337-51. http://dx.doi.org/10.1177/0021998303034307

Okutan B. The effects of geometric parameters on the failure strength for pin-loaded multi-directional fiberglass reinforced epoxy laminate. Compos: Part B 2002; 33: 567-78. http://dx.doi.org/10.1016/S1359-8368(02)00054-9

Downloads

Published

2013-04-04

How to Cite

Harsha, H., Murugesh, M., & Bharath, K. (2013). Influence of Filler Materials on Pinned Joints of Woven Glass Fiber Reinforced Epoxy Composites . Journal of Composites and Biodegradable Polymers, 1(1), 47–55. https://doi.org/10.12974/2311-8717.2013.01.01.6

Issue

Section

Articles